UNS N06600 - EN/DIN 2.4816 – NiCr15Fe
UNS N06600 is a Nickel-Chromium Alloy with a good resistance to oxidation and corrosion at high temperatures. Due to this characteristics it is often used for furnace components and in the nuclear engineering.
As one of the worldwide biggest manufacturer and stockist of Alloy UNS N06600 we supply this Material to many different industries such as oil and gas, power generation, petrochemical and other industries.
TPS Technitube Roehrenwerke GmbH supplies UNS N06600 in a big variety of forms incl.:
Seamless Tubes & Pipes
Welded Tubes and Pipes
Buttweld Fittings
Forged Fittings
Flanges and Forgings
Plates, Sheets and Bars
Mechanical values
Annealed condition:
Hot-worked or Hot-worked annealed, 5 in. (127 mm) in outside diameter and under
| Tensile Strength, min, MPa: | 550 | |
| Yield Strength (0,2% offset), min, MPa: | 205 | |
| Elongation in 2 in. or 50 mm ( or 4 D), min, %: | 35 | |
Annealed condition:
Cold-worked annealed, 5 in. (127 mm) in outside diameter and under
| Tensile Strength, min, MPa: | 550 | |
| Yield Strength (0,2% offset), min, MPa: | 240 | |
| Elongation in 2 in. or 50 mm ( or 4 D), min, %: | 30 | |
Mechanical values
Annealed condition:
Hot-worked or Hot-worked annealed, over 5 in. (127 mm) in outside diameter
| Tensile Strength, min, MPa: | 515 |
| Yield Strength (0,2% offset), min, MPa: | 170 |
| Elongation in 2 in. or 50 mm ( or 4 D), min, %: | 35 |
Annealed condition:
Cold-worked annealed, over 5 in. (127 mm) in outside diameter
| Tensile Strength, min, MPa: | 550 |
| Yield Strength (0,2% offset), min, MPa: | 205 |
| Elongation in 2 in. or 50 mm ( or 4 D), min, %: | 35 |
Chemical Analysis
| C | = 0,10% max | Mn | = 1,00% max |
| S | = 0,015% max | Si | = 0,50% max |
| Ni | = 72,00% min | Cu | = 0,50% max |
| Fe | = 10,00% max | Si | = 0,50% max |
Please select your country to contact us
TPS-Technitube Röhrenwerke GmbH
Julius-Saxler-Str. 7 | 54550 Daun/Germany
Tel.: +49 65 92 71 20 | Fax: +49 65 92 1305
www.technistock.de | www.tpsd.de | E-Mail: service@tpsd.de