UNS S31803/UNS S32205 | Techniduplex TD2205

A widely used duplex steel combining high strength and corrosion resistance in various organic acids, an organic acids, aggressive cooling waters and hydrous H2S/NaCl mixtures. With a near equal mix of austenite and ferrite, they give yield strength 30% higher and tensile strengths marginally higher than comparable nitrogen containing austenitic. High resistance to general corrosion and specifically to pitting and crevice corrosion. Their resistance to stress-corrosion cracking in neutral chlorides is superior to that of the austenite. In high chloride, acidic or moderately sour environments where hydrogen or sulphide stress cracking is more likely, higher alloyed austenitic need also to be considered. Impact values are high and transition temperatures of base materials vary around – 50°C. However, the proportion and orientation of ferrite in welds and base materials may significantly affect toughness at sub zero temperatures. Exposure to moderate and high temperatures and less rapid cooling may cause embrittlement.

  • Heat Exchanger Tubes
  • Boiler Tubes & Pipes
  • Line Pipes
  • Hydraulic Tubes
  • Instrumentation Tubes
  • Structural Pipes
  • Mechanical Tubes & Pipes

TPS Technitube supplies UNS S31803/UNS S32205 | Techniduplex TD2205 in a big variety of forms incl.:




Chemical Composition

C = 0.03 % max S = 0.020 % max
Si = 1.00 % max Ni = 4.50-6.50 %
Mn = 2.00 % max Cr = 21.0-23.0 %
P = 0.030 % max Mo = 2.50-3.50 %
N = 0.08-0.20 %

Mechanical properties all at room temperature

Elongation in 2 in or 50 mm, (or 4D), min 40%
YS min
KSI (MPa) = 65[450]
TS min
KSI [MPa] = 90[620]
El. min 25
max 290
C max = 30.5



Please select your country to contact us

Contact Us

    I agree that my data may be used for processing your messages and will be deleted at the very latest six month after my enquiry is processed.

    TPS-Technitube Röhrenwerke GmbH
    Julius-Saxler-Str. 7 | 54550 Daun/Germany
    Tel.: +49 65 92 71 20 | Fax: +49 65 92 1305 | | E-Mail: